Q: Our screws snap – what is wrong?
A: You probably use ther incorrect steel grade. Or that the hydrogene content in the material is too high, which leads to hydrogene brittleness. This can be determined by steel grade and hydrogene analyses.

Q: The tools break, in process – what do we need to do?
A: This is probably due to an incorrect steel grade or incorrect hardening. This can be determined by carbon and steel grade anlyses.

Q: We have a small metal flake. Can it be analysed?
A: Yes. We can do a survey analyses.

Q: We have observed a coating. What is it?
A: Let’s do a survey analyses.

Q: Can you determine if there is nickel in jewelry?
A: Yes. We can also determine if the fine metal lives up to its promises (is it really silver…?)